VALOX™ Resin IQ507

SI

| British

| Metric

| PDF

Americas: COMMERCIAL

Valox iQ507 resin: Environmentally responsible, sustainable, and low carbon footprint resin that is 30% glass fiber reinforced PBT+PC alloy. Valox iQ507 offers good mechanical and thermal characteristics, along with reduced warpage characteristics.

Property

MECHANICAL

Tensile Stress, yld, Type I, 5 mm/min

1070

kgf/cm²

ASTM D 638

Tensile Stress, brk, Type I, 5 mm/min

1070

kgf/cm²

ASTM D 638

Tensile Stress, brk, Type I, 10 mm/min

1340

kgf/cm²

SABIC - Japan Method

Tensile Strain, yld, Type I, 5 mm/min

1

%

ASTM D 638

Tensile Strain, brk, Type I, 5 mm/min

1

%

ASTM D 638

Tensile Strain, brk, Type I, 10 mm/min

7

%

SABIC - Japan Method

Tensile Modulus, 5 mm/min

130500

kgf/cm²

ASTM D 638

Flexural Stress, yld, 1.3 mm/min, 50 mm span

1990

kgf/cm²

ASTM D 790

Flexural Modulus, 1.3 mm/min, 50 mm span

92400

kgf/cm²

ASTM D 790

Hardness, Rockwell R

119

-

ASTM D 785

Tensile Stress, yield, 5 mm/min

96

MPa

ISO 527

Tensile Stress, break, 5 mm/min

96

MPa

ISO 527

Tensile Strain, yield, 5 mm/min

1

%

ISO 527

Tensile Strain, break, 5 mm/min

1

%

ISO 527

Tensile Modulus, 1 mm/min

10200

MPa

ISO 527

Flexural Stress, yield, 2 mm/min

187

MPa

ISO 178

Flexural Modulus, 2 mm/min

8910

MPa

ISO 178

IMPACT

Izod Impact, unnotched, 23°C

60

cm-kgf/cm

ASTM D 4812

Izod Impact, notched, 23°C

8

cm-kgf/cm

ASTM D 256

Izod Impact, notched, -30°C

7

cm-kgf/cm

ASTM D 256

Instrumented Impact Total Energy, 23°C

71

cm-kgf

ASTM D 3763

Izod Impact, notched 80*10*4 +23°C

8

kJ/m²

ISO 180/1A

Izod Impact, notched 80*10*4 -30°C

7

kJ/m²

ISO 180/1A

Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm

21

kJ/m²

ISO 179/1eA

THERMAL

Vicat Softening Temp, Rate B/50

192

°C

ASTM D 1525

HDT, 1.82 MPa, 3.2mm, unannealed

182

°C

ASTM D 648

CTE, -40°C to 40°C, flow

2.1E-05

1/°C

ASTM E 831

CTE, -40°C to 40°C, xflow

8.1E-05

1/°C

ASTM E 831

CTE, -40°C to 40°C, flow

2.1E-05

1/°C

ISO 11359-2

CTE, -40°C to 40°C, xflow

8.1E-05

1/°C

ISO 11359-2

Vicat Softening Temp, Rate B/50

192

°C

ISO 306

Vicat Softening Temp, Rate B/120

190

°C

ISO 306

HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm

212

°C

ISO 75/Bf

HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm

186

°C

ISO 75/Af

PHYSICAL

Specific Gravity

1.51

-

ASTM D 792

Mold Shrinkage, flow, 3.2 mm (5)

0.1 - 0.4

%

SABIC Method

Mold Shrinkage, xflow, 3.2 mm (5)

0.4 - 0.8

%

SABIC Method

Melt Flow Rate, 250°C/5.0 kgf

50

g/10 min

ASTM D 1238

Density

1.51

g/cm³

ISO 1183

Water Absorption, (23°C/sat)

0.1

%

ISO 62

Moisture Absorption (23°C / 50% RH)

0.08

%

ISO 62

Melt Volume Rate, MVR at 220°C/5.0 kg

43

cm³/10 min

ISO 1133

Melt Volume Rate, MVR at 250°C/5.0 kg

38

cm³/10 min

ISO 1133

Source GMD, last updated:2007/11/01

Processing

Injection Molding

Drying Temperature

120

°C

Drying Time

3 - 4

hrs

Drying Time (Cumulative)

12

hrs

Maximum Moisture Content

0.02

%

Melt Temperature

250 - 265

°C

Nozzle Temperature

245 - 260

°C

Front - Zone 3 Temperature

250 - 265

°C

Middle - Zone 2 Temperature

245 - 260

°C

Rear - Zone 1 Temperature

240 - 255

°C

Mold Temperature

65 - 90

°C

Back Pressure

0.3 - 0.7

MPa

Screw Speed

50 - 80

rpm

Shot to Cylinder Size

40 - 80

%

Vent Depth

0.025 - 0.038

mm