XENOY™ Resin 1760E

SI

| British

| Metric

| PDF

Americas: COMMERCIAL

11% Glass Reinforced alloy. Impact/chemical resistant. Excellent physical property retention in automotive exteriors. High flow version of Xenoy 1760 resin.

Property

MECHANICAL

Tensile Stress, yld, Type I, 5 mm/min

850

kgf/cm²

ASTM D 638

Tensile Stress, brk, Type I, 5 mm/min

850

kgf/cm²

ASTM D 638

Tensile Strain, yld, Type I, 5 mm/min

3

%

ASTM D 638

Tensile Strain, brk, Type I, 5 mm/min

3

%

ASTM D 638

Tensile Modulus, 5 mm/min

54100

kgf/cm²

ASTM D 638

Flexural Stress, yld, 1.3 mm/min, 50 mm span

1330

kgf/cm²

ASTM D 790

Flexural Modulus, 1.3 mm/min, 50 mm span

39900

kgf/cm²

ASTM D 790

Tensile Stress, yield, 5 mm/min

84

MPa

ISO 527

Tensile Stress, break, 5 mm/min

84

MPa

ISO 527

Tensile Strain, yield, 5 mm/min

3

%

ISO 527

Tensile Strain, break, 5 mm/min

3

%

ISO 527

Tensile Modulus, 1 mm/min

4800

MPa

ISO 527

Flexural Stress, yield, 2 mm/min

133

MPa

ISO 178

Flexural Modulus, 2 mm/min

4010

MPa

ISO 178

IMPACT

Izod Impact, notched, 23°C

6

cm-kgf/cm

ASTM D 256

Izod Impact, notched, -30°C

6

cm-kgf/cm

ASTM D 256

Instrumented Impact, Energy @ peak, -20°C

40

cm-kgf

ASTM D 3763

Instrumented Impact Energy @ peak, -30

30

cm-kgf

ASTM D 3763

Instrumented Impact Total Energy, 23°C

81

cm-kgf

ASTM D 3763

Instrumented Impact Total Energy, -30°C

30

cm-kgf

ASTM D 3763

Izod Impact, notched 80*10*4 +23°C

3

kJ/m²

ISO 180/1A

Izod Impact, notched 80*10*4 -30°C

3

kJ/m²

ISO 180/1A

Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm

12

kJ/m²

ISO 179/1eA

THERMAL

Vicat Softening Temp, Rate B/50

121

°C

ASTM D 1525

HDT, 1.82 MPa, 3.2mm, unannealed

125

°C

ASTM D 648

HDT, 1.82 MPa, 6.4 mm, unannealed

116

°C

ASTM D 648

CTE, -40°C to 40°C, flow

3.9E-05

1/°C

ASTM E 831

CTE, -40°C to 40°C, xflow

7.6E-05

1/°C

ASTM E 831

CTE, -40°C to 40°C, flow

3.9E-05

1/°C

ISO 11359-2

CTE, -40°C to 40°C, xflow

7.6E-05

1/°C

ISO 11359-2

Vicat Softening Temp, Rate B/50

135

°C

ISO 306

Vicat Softening Temp, Rate B/120

130

°C

ISO 306

HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm

101

°C

ISO 75/Af

PHYSICAL

Specific Gravity

1.3

-

ASTM D 792

Mold Shrinkage, flow, 3.2 mm (5)

0.4 - 0.6

%

SABIC Method

Mold Shrinkage, xflow, 3.2 mm (5)

0.4 - 0.6

%

SABIC Method

Melt Flow Rate, 250°C/5.0 kgf

15

g/10 min

ASTM D 1238

Density

1.3

g/cm³

ISO 1183

Water Absorption, (23°C/sat)

0.5

%

ISO 62

Moisture Absorption (23°C / 50% RH)

0.15

%

ISO 62

Melt Volume Rate, MVR at 265°C/5.0 kg

27

cm³/10 min

ISO 1133

Source GMD, last updated:2010/06/29

Processing

Injection Molding

Drying Temperature

110

°C

Drying Time

4 - 6

hrs

Drying Time (Cumulative)

8

hrs

Maximum Moisture Content

0.02

%

Melt Temperature

260 - 280

°C

Nozzle Temperature

255 - 275

°C

Front - Zone 3 Temperature

260 - 280

°C

Middle - Zone 2 Temperature

255 - 275

°C

Rear - Zone 1 Temperature

250 - 270

°C

Mold Temperature

65 - 95

°C

Back Pressure

0.3 - 0.6

MPa

Screw Speed

50 - 80

rpm

Shot to Cylinder Size

50 - 80

%

Vent Depth

0.013 - 0.02

mm