| TYPICAL PROPERTIES (1) |
|
MECHANICAL
|
Value |
Unit |
Standard |
|
Tensile Stress, yld, Type I, 50 mm/min
|
540
|
kgf/cm²
|
ASTM D 638
|
|
Tensile Stress, brk, Type I, 50 mm/min
|
520
|
kgf/cm²
|
ASTM D 638
|
|
Tensile Strain, yld, Type I, 50 mm/min
|
4
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I, 50 mm/min
|
120
|
%
|
ASTM D 638
|
|
Tensile Modulus, 50 mm/min
|
22900
|
kgf/cm²
|
ASTM D 638
|
|
Tensile Modulus, 5 mm/min
|
22900
|
kgf/cm²
|
ASTM D 638
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
850
|
kgf/cm²
|
ASTM D 790
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
20600
|
kgf/cm²
|
ASTM D 790
|
|
Tensile Stress, yield, 50 mm/min
|
50
|
MPa
|
ISO 527
|
|
Tensile Stress, break, 50 mm/min
|
50
|
MPa
|
ISO 527
|
|
Tensile Strain, yield, 50 mm/min
|
4
|
%
|
ISO 527
|
|
Tensile Strain, break, 50 mm/min
|
120
|
%
|
ISO 527
|
|
Tensile Modulus, 1 mm/min
|
2050
|
MPa
|
ISO 527
|
|
Flexural Stress, yield, 2 mm/min
|
80
|
MPa
|
ISO 178
|
|
Flexural Modulus, 2 mm/min
|
2000
|
MPa
|
ISO 178
|
|
IMPACT
|
Value |
Unit |
Standard |
|
Izod Impact, notched, 23°C
|
72
|
cm-kgf/cm
|
ASTM D 256
|
|
Izod Impact, notched, -30°C
|
54
|
cm-kgf/cm
|
ASTM D 256
|
|
Izod Impact, notched, -40°C
|
30
|
cm-kgf/cm
|
ASTM D 256
|
|
Instrumented Impact Total Energy, 23°C
|
611
|
cm-kgf
|
ASTM D 3763
|
|
Izod Impact, notched 80*10*4 +23°C
|
50
|
kJ/m²
|
ISO 180/1A
|
|
Izod Impact, notched 80*10*4 -30°C
|
30
|
kJ/m²
|
ISO 180/1A
|
|
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm
|
55
|
kJ/m²
|
ISO 179/1eA
|
|
THERMAL
|
Value |
Unit |
Standard |
|
Vicat Softening Temp, Rate B/50
|
122
|
°C
|
ASTM D 1525
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
84
|
°C
|
ASTM D 648
|
|
HDT, 0.45 MPa, 6.4 mm, unannealed
|
107
|
°C
|
ASTM D 648
|
|
HDT, 1.82 MPa, 6.4 mm, unannealed
|
99
|
°C
|
ASTM D 648
|
|
CTE, -40°C to 40°C, flow
|
9.5E-05
|
1/°C
|
ASTM E 831
|
|
CTE, -40°C to 40°C, xflow
|
9.E-05
|
1/°C
|
ASTM E 831
|
|
CTE, -40°C to 40°C, flow
|
9.5E-05
|
1/°C
|
ISO 11359-2
|
|
CTE, -40°C to 40°C, xflow
|
9.E-05
|
1/°C
|
ISO 11359-2
|
|
Vicat Softening Temp, Rate B/50
|
120
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate B/120
|
125
|
°C
|
ISO 306
|
|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
|
75
|
°C
|
ISO 75/Af
|
|
Relative Temp Index, Elec
|
75
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/impact
|
75
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/o impact
|
75
|
°C
|
UL 746B
|
|
PHYSICAL
|
Value |
Unit |
Standard |
|
Specific Gravity
|
1.21
|
-
|
ASTM D 792
|
|
Specific Volume
|
0.83
|
cm³/g
|
ASTM D 792
|
|
Mold Shrinkage, flow, 3.2 mm (5)
|
0.8 - 1
|
%
|
SABIC Method
|
|
Mold Shrinkage on Tensile Bar, xflow (2) (5)
|
0.8 - 1
|
%
|
SABIC Method
|
|
Density
|
1.22
|
g/cm³
|
ISO 1183
|
|
Water Absorption, (23°C/sat)
|
0.5
|
%
|
ISO 62
|
|
Moisture Absorption (23°C / 50% RH)
|
0.15
|
%
|
ISO 62
|
|
Melt Flow Rate, 250°C/5.0 kg
|
16
|
g/10 min
|
ISO 1133
|
|
Melt Volume Rate, MVR at 250°C/5.0 kg
|
15
|
cm³/10 min
|
ISO 1133
|
|
ELECTRICAL
|
Value |
Unit |
Standard |
|
Arc Resistance, Tungsten {PLC}
|
5
|
PLC Code
|
ASTM D 495
|
|
Hot Wire Ignition {PLC)
|
3
|
PLC Code
|
UL 746A
|
|
High Voltage Arc Track Rate {PLC}
|
0
|
PLC Code
|
UL 746A
|
|
High Ampere Arc Ign, surface {PLC}
|
0
|
PLC Code
|
UL 746A
|
|
Comparative Tracking Index (UL) {PLC}
|
1
|
PLC Code
|
UL 746A
|
|
FLAME CHARACTERISTICS
|
Value |
Unit |
Standard |
|
UL Recognized, 94HB Flame Class Rating (3)
|
1.5
|
mm
|
UL 94
|
|
UV-light, water exposure/immersion
|
F2
|
-
|
UL 746C
|